5A02 Aluminium sheet is Al - Mg series anti-rust aluminum, compared with 3a21, 5A02 aluminum alloy high strength especially has high fatigue strength; Plastic with high corrosion resistance, in this respect is similar to 3a21; Cannot strengthening heat treatment, with resistance welding and atomic hydrogen welding, argon arc welding with form crystallization crack tendency; Alloy in cold work hardening and half cold work hardening condition can be better machinability, annealing state cutting can be bad, can be polished.

5A02 aluminum chemical composition
Si Si: 0.40
Iron Fe: 0.40
Copper Cu: 0.10
Chromium manganese Mn: 0.15-0.40 or Cr: 0.15 to 0.40
Magnesium Mg: 2.0 to 2.8
Silicon iron + Fe + Si: 0.60
Ti Ti: 0.15
Al: aluminum allowance
Other:
Completed a single: 0.05:0.05
5A02 aluminum plate mechanical properties
Tensile strength of sigma b (MPa) : 147 or less
Elongation delta (%) : 14 or higher
Note: the pattern plate mechanical properties at room temperature
5A02 aluminum plate heat treatment specification
1) homogenizing annealing: heating to 440 ℃. Insulation 12 ~ 14 h; Air cooling.
2) rapid annealing: heating to 350 ~ 350 ℃. The heat preservation time of 30 ~ 120 min; Air or water.
3) high temperature annealing: heating to 350 ~ 350 ℃. Thickness or < 6 mm or 6 mm, heat preservation time is 2 ~ 10 min or 10 ~ 30 min; Air cooling.
4) low temperature annealing: heating to 250 ~ 300 ℃ and 150 ~ 180 ℃; Holding time is 1 ~ 2 h, air cooling
Status: aluminium and aluminium alloy decorative pattern plate (O)